Solid electrolytes containing polysiloxane acrylates

ABSTRACT

This invention is directed to the use of polysiloxane acrylates in solid electrolytes containing a solid polymeric matrix. The solid electrolytes are used in electrochemical cells for secondary batteries.

BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention is directed to solid electrolytes produced by polymerization of polysiloxane acrylates. This invention is further directed to solid electrolytic cells (batteries) containing an anode, a cathode and a solid electrolyte containing a solvent, an inorganic ion salt and a polymer matrix, which includes polysiloxane acrylate.

2. State of the Art

Electrolytic cells containing an anode, a cathode and a solid, solvent-containing electrolyte are known in the art and are usually referred to as "solid batteries". These cells offer a number of advantages over electrolytic cells containing a liquid electrolyte (i.e., "liquid batteries") including improved safety features.

The solid, solvent-containing electrolyte employed in such solid batteries has heretofore contained either an inorganic matrix or an organic polymeric matrix as well as a suitable inorganic ion salt. Because of their expense and difficulty in forming into a variety of shapes, inorganic non-polymeric matrices are, however, not preferred, and the art typically has employed a solid electrolyte containing an organic or inorganic polymeric matrix.

Suitable organic polymeric matrices are well known in the art and are typically organic homopolymers obtained by polymerization of a suitable organic monomer as described, for example, in U.S. Pat. No. 4,908,283 or copolymers obtained by polymerization of a mixture of organic monomers. Reference is made to Fiona M. Gray, "Solid Polymer Electrolytes", VCH Publishers, Inc., New York, N.Y. , 1991, the disclosure of which is incorporated herein in its entirety.

Additionally, suitable organic monomers preferably contain at least one heteroatom capable of forming donor acceptor bonds with inorganic cations (e.g., alkali ions). When polymerized, these compounds form a polymer suitable for use as an ionically conductive matrix in a solid electrolyte.

The solid electrolytes also contain an electrolyte solvent (plasticizer) which is added to the matrix primarily in order to enhance the solubility of the inorganic ion salt in the solid electrolyte and thereby increase the conductivity of the electrolytic cell. In this regard, the solvent requirements of the solvent used in the solid electrolyte have been art recognized to be different from the solvent requirements in liquid electrolytes. For example, solid electrolytes require a lower solvent volatility as compared to the solvent volatilities permitted in liquid electrolytes.

Suitable electrolyte solvents well known in the art for use in such solid electrolytes include, by way of example, propylene carbonate, ethylene carbonate, β-butyrolactone, tetrahydrofuran, glyme (dimethoxyethane), diglyme, triglyme, tetraglyme, dimethylsulfoxide, dioxolane, sulfolane and the like.

The solid, solvent-containing electrolyte has typically been formed by one of two methods. In one method, the solid matrix is first formed and then a requisite amount of this material is dissolved in a volatile solvent. Requisite amounts of the inorganic ion salt and the electrolyte solvent (e.g., a mixture of a glyme and an organic carbonate) are then added to the solution. This solution is then placed on the surface of a suitable substrate (e.g., the surface of a cathode) and the volatile solvent is removed to provide for the solid electrolyte.

In the other method, a monomer or partial polymer of the polymeric matrix to be formed is combined with appropriate amounts of the inorganic ion salt and substrate (e.g., the surface of the cathode) and the monomer is polymerized or cured (or the partial polymer is then further polymerized or cured) by conventional techniques (e.g., heat, ultraviolet radiation, electron beams, etc.) so as to form the solid, solvent-containing electrolyte.

A number of studies of siloxane-based polymer electrolytes have been reported in the literature. The literature has been reviewed by Gray, ibid., pp. 98-101.

There is need for improvement in several areas of the art. The physical properties of the electrolytes cannot usually be tailored easily by mere control of the polymerization process. For example, the solid polymeric matrix of the electrolytes must have a certain degree of flexibility and swellability in order to function properly in the cell. If the cross-linking density of the matrix is too high, the resulting polymer network is very tight, resulting in minimal flexibility and swellability.

SUMMARY OF THE INVENTION

The present invention is directed, in part, to a novel solid polymeric electrolyte for use in secondary batteries. The solid electrolyte of this invention comprises a solid polymeric matrix, an electrolyte solvent and an inorganic ion salt, wherein the solid polymeric matrix comprises a polymerized polysiloxane acrylate. The polysiloxane acrylate is polymerized (sometimes termed "cured") by exposure to actinic radiation. The polysiloxane acrylate is the reaction product of an acrylic acid, CH₂ =CR¹ C(O)OH, wherein R¹ is H or an alkyl group of from 1 to 4 carbon atoms, and polysiloxane. Preferably, the polysiloxane acrylate is of molecular weight of from about 150 to about 5,000.

Preferably, the polysiloxane acrylate is the reaction product of an acrylic acid and a polysiloxane consisting of from about 3 to about 50 or more repeating units selected from the group consisting of ##STR1## and mixtures thereof, wherein n is 0 or an integer between 1 and 50, R¹, and R² are independently selected alkyl groups of from 1 to 4 carbon atoms, R³ is an alkylene group of from 1 to 4 carbon atoms and R⁴ is alkylene group of from 1 to 6 carbon atoms.

In another aspect of the present invention, an electrochemical cell comprises an anode composed of a compatible anodic material, a cathode composed of a compatible cathodic material, and interpose therebetween, a solid electrolyte comprising: a solid polymer matrix, an electrolyte solvent, and an inorganic ion salt, wherein said polymeric matrix comprises a polymerized polysiloxane acrylate. In another aspect of the present invention, a battery comprises a plurality of such electrochemical cells.

In yet another aspect of the present invention, a method of making a solid electrolyte comprises the steps of forming a mixture comprising a compatible electrolyte solvent, an inorganic ion salt and a polysiloxane acrylate and exposing said mixture to actinic radiation.

The solid electrolyte of the present invention contains a polymeric matrix composed of polysiloxane acrylate which is optionally copolymerized (i.e., crosslinked or cured) with at least one other polymer precursor selected from the group consisting of polyethylene oxide, polypropylene oxide, polyethyleneimine, polyepichlorohydrin, an acryloyl-derivatized and an acryloyl-derivatized poly(oxyalkylene) oxide.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

As noted above, this invention is directed to solid, solvent-containing electrolytes which employ a specific solid, polymeric, ion-conducting matrix.

Separation of the relatively non-polar polysiloxane acrylate matrix from the polar electrolyte solvent is overcome by the inclusion of larger amounts of other polymer precursors prior to the curing step as disclosed herein, by variation of the molecular weight of the polysiloxane acrylate, and by the choice of siloxane repeating units as taught herein.

The incorporation of the polysiloxane acrylate of the invention into the polymer backbone of the solid polymeric matrix provides the advantages of increased chemical inertness due to the presence of the siloxane repeating units. The increased inertness can lead to increased battery life since there is less breakdown of the solid polymeric matrix during repeated recharging of the battery. However, prior to describing this invention in detail, the following terms will first be defined.

Definitions

As used herein, the following terms have the following meanings.

The term "siloxane" refers to a molecule containing SiOSi group(s). As always, Si is quadfivalent, and does not form multiple bonds, e.g., hexachlorosiloxane, Cl₃ SiOSiCl₃ (produced by the controlled hydrolysis of SiCl₄ in air at high temperature). "Polysiloxanes" frequently, and misleadingly, referred to as "silicones" are prepared by hydrolysis of alkyl silicon or aryl silicon halides. The starting materials are themselves made by heating silicon and alkyl or aryl halides in the presence of copper at 250° C. to 280° C. Hydrolysis of the silicon halides gives the corresponding unstable silanols which undergo condensation to form siloxane linkages. The hydrolysis of dichlorides gives linear polysiloxanes while the hydrolysis of trichlorides gives branched polysiloxanes. Since the halides produce an abundance of low molecular weight cyclic polysiloxanes, it is preferable to obtain high molecular weight polysiloxanes by the acid or base-catalyzed ring-opening reactions. Acrylic acid may be utilized for a chain-terminating reaction, or to cap the polysiloxanes with acrylate. The polymerizing siloxanes may also be reacted with poly(oxyalkylene) glycols to incorporate hydroxyl groups which are later used to form the acrylate by reaction with acrylic acid.

The polysiloxane acrylate of the invention may be an acrylate, a diacrylate, or a multi-acrylate, depending on the reaction conditions, the reactants, and the number of reaction sites for acrylic acid present in the polysiloxane. The diacrylates are preferred.

The predominately "comb-branched" polysiloxanes are preferred, although they may incorporate minor amounts of cyclic and linear siloxanes, their properties are predominantly elastomeric. Consequently, the polysiloxanes of the present invention consist essentially of repeating units selected from the group consisting of: ##STR2## and mixtures thereof. R¹ and R² are independently alkyl groups of from 1 to 4 carbon atoms, R³ is an alkylene group of from 1 to 4 carbon atoms, R⁴ is an alkylene group of from 1 to 6 carbon atoms, and n is 0 or an integer from about 1 to 50. The number of units present in the polysiloxane will number from about 3 to about 100, preferably from about 3 to about 50.

Reference is made to M. P. Stevens, "Polymer Chemistry" Oxford University Press, New York, 1990, pages 489 to 493; P. G. Hall et al. Polym. Commun. 27 (1986), page 98; D. Fish et al., Makro Mol. Chem. Rapid Commun. 7 (1986), p. 115; R. S. Spintiler et al., J. Am. Chem. Soc. 110 (1988); p. 3036; D. Fish et al., Br. Polym. J. 20 (1988), p. 281; the disclosure of each of which is incorporated by reference herein in its entirety.

The chain terminating groups of the polysiloxanes before reaction with acrylate acid are hydroxyl, chloride, alkyl, alkanol, aryl and the like. Consequently, the term "polysiloxane" refers to molecules formed from the aforementioned siloxane units, and variously terminated as described.

The term "acrylic acid" refers to the acid CH₂ =CR¹ C(O)OH, its acid halides, its anhydrides, and other acrylic reactants which provide a polysiloxane acrylate upon reaction with polysiloxane. Typical reactions carded out under conditions known to chemists include the reaction of a silanol-terminated polysiloxane with acrylic acid, or acrylic chloride, and the reaction of a chloropolysiloxane with acrylic acid.

Generally, the polysiloxane acrylate has a number average molecular weight of less than about 15,000, desirably less than about 10,000 and preferably less than about 8,000, In a highly preferred embodiment, the monomer has a molecular weight of between about 150 and about 5,000. In all cases, the bulk of the molecular weight is contributed by the siloxane groups with the acrylate groups constituting end caps.

The term "solid polymeric matrix" refers to an ion-conductive matrix formed by polymerizing polymer precursor (i.e., a prepolymer, oligomer or monomer) containing at least one heteroatom capable of forming donor acceptor bonds with inorganic cations derived from inorganic ion salts under conditions such that the resulting polymer is useful in preparing solid electrolytes. Solid polymeric matrices are well known in the art and are described, for example, in U.S. Pat. No. 4,908,283 and in U.S. Pat. No. 4,925,751 both of which are incorporated herein by reference in their entirety. Solid polymeric matrices are typically formed by the polymerization or copolymerization (i.e., crosslinking) of polymer precursors.

Suitable organic monomers which are copolymerizable with the polysiloxane acrylates of the invention include, by way of example, ethylene oxide, propylene oxide, ethyleneimine, epichlorohydrin, ethylene succinate, the various methane acrylates and an acryloyl-derivatized alkylene oxide containing an acryloyl group.

The term "inorganic ion salt" refers to any ion conducting inorganic salt which is suitable for use in a solid electrolyte. Representative examples are alkali metal salts of less mobile anions of weak bases having a large anionic radius. Examples of such anions are I⁻, Br⁻, SCN⁻, ClO₄ ⁻, BF₄ ⁻, PF₆ ⁻, AsF₆ ⁻, CF₃ COO⁻, CF₃ SO₃ ⁻, etc. Specific examples of suitable inorganic ion salts include LiClO₄, LiI, LiSCN, LiBF₄, LiAsF₆, LiCF₃ SO₃, LiPF₆, Li[N(SO₂ CF₃)₂ ], Li[C(SO₂ CF₃)₃ ]NaI, NaSCN, KI and the like. The inorganic ion salt preferably contains at least one atom of Li, Na, K or Mg.

The term "electrolyte solvent" refers to the solvent (i.e., plasticizer) added to the electrolyte and/or the cathode for the purpose of solubilizing the inorganic ion salt. Preferred are the various polar aprotic solvents. Examples of polar aprotic solvents useful in the invention are polar solvents such as propylene carbonate, ethylene carbonate, butylene carbonate, β-butyrolactone, tetrahydrofuran, 2-methyltetrahydrofuran, and 1,3-dioxolane.

A particularly preferred solvent is a mixture of an organic carbonate and triglyme as disclosed in U.S. patent application Ser. No. 07/918,509, filed Jul. 22, 1992, and entitled "SOLID, SOLVENT-CONTAINING ELECTROLYTES AND ELECTROLYTIC CELLS PRODUCED THEREFROM" which application is incorporated herein by reference in its entirety.

In a highly preferred embodiment, the electrolyte solvent is a mixture of propylene carbonate and a glyme in a ratio (w/w) of from about 10:1 to about 1:4. In a most preferred embodiment, the ratio is 4:1 propylene carbonate/triglyme.

If the solid polymeric matrix is formed by radiation polymerization of the polysiloxane acrylate, then the solvent should be radiation inert at least up to the levels of radiation employed. If the solid polymeric matrix is formed by thermal polymerization, the solvent should be thermally inert at least up to the temperatures of thermal polymerization. Additionally, the solvent should not scavenge free radicals.

The term "cured" or "cured product" refers to the treatment of the polymer precursors (or partial polymer) under polymerization conditions (including cross-linking) so as to form a solid polymeric matrix. Suitable polymerization conditions are well known in the art and include, by way of example, heating the monomer, irradiating the monomer with actinic radiation i.e, UV light, electron beams (liB), etc. The presence of acrylic groups in the siloxane acrylates allows polymerization by UV or EB radiation.

The term "dectrolytic cell" or "electrochemical cell" refers to a composite containing an anode, a cathode, and an ion-conducting electrolyte interposed therebetween.

The anode is typically comprised of a compatible anodic material which is any material which functions as an anode in a solid electrolytic cell. Such compatible anodic materials are well known in the art and include, by way of example, lithium, lithium alloys, such as alloys of lithium with aluminum, mercury, manganese, iron, zinc, and the like, and intercalation based anodes such as carbon, tungsten oxides, and the like.

The cathode is typically comprised of a compatible cathodic material (i.e., insertion compounds) which is any material which functions as a positive pole in a solid electrolytic cell. Such compatible cathodic materials are well known in the art and include, by way of example, manganese oxides, molybdenum oxides, vanadium oxides, sulfides of titanium, molybdenum and niobium, the various chromium oxides, copper oxides, lithiated cobalt oxides, lithiated manganese oxides, and the like. The particular compatible cathodic material employed is not critical.

In one preferred embodiment, the compatible cathodic material is mixed with an electroconductive material including, by way of example, graphite, powdered carbon, powdered nickel, metal particles, conductive polymers (i.e., characterized by a conjugated network of double bonds like polypyrrole and polyacetylene), and the like, and a polymeric binder to form under pressure a positive cathodic plate.

In another preferred embodiment, the cathode is prepared from a cathode paste which comprises from about 35 to 65 weight percent of a compatible cathodic material; from about 1 to 20 weight percent of an electroconductive agent; from about 0 to 20 weight percent of polyethylene oxide having a number average molecular weight of at least 100,000; from about 10 to 50 weight percent of the electrolyte solvent; and from at least about 5 weight percent to 30 weight percent of a solid polymeric matrix which includes the polysiloxane acrylate above. (All weight percents are based on the total weight of the cathode.)

The cathode paste is typically spread onto a suitable support such as a current collector and then cured by EB to provide for a solid positive cathodic plate. The cathode (excluding the support) generally has a thickness of from about 20 to about 150 microns.

Current collectors are well known in the art some of which are commercially available. One particularly preferred current collector for the cathode is a roughened nickel (electrolytically deposited nickel) on nickel current collector (available as CF18/NiT from Fukuda Metal Foil & Powder Company, Ltd., Kyoto, Japan). Another preferred current collector employs a sheet of aluminum foil. The current collector is preferably attached to the surface of the cathode not facing the electrolyte but can also be attached to the anode. When the current collector is attached to the cathode, the cathode is interposed between the electrolyte and the current collector.

In still another preferred embodiment, the electrolyte solvent and the cathode solvent are identical.

The term "urethane acrylate" refers to urethane diacrylate. The polysiloxane acrylate of the invention can be used as a complete or partial replacement for the urethane acrylate in the polymer matrices taught in the art.

In an embodiment, the solid, solvent-containing electrolyte is then prepared by combining a polysiloxane acrylate or a mixture of polysiloxane acrylates, and optimally one other organic monomer or partial polymer, with an inorganic ion salt and the electrolyte solvent. The resulting composition is then uniformly coated onto a suitable substrate (e.g., aluminum foil, a glass plate, a lithium anode, a cathode, etc.) by means of a roller, a doctor blade, a bar coater, a silk screen or spinner to obtain a film of this composition or its solution. In some cases, it may be necessary to heat the composition so as to provide for a coatable material.

Preferably, the amount of material coated onto the substrate is an amount sufficient so that after curing, the resulting solid, solvent-containing electrolyte has a thickness of no more than about 250 microns (μm). Preferably, the solid, solvent-containing electrolyte has a thickness of from about 25 to about 100 microns. The actual thickness chosen is a function of the particular application and can readily be determined by one skilled in the art.

The electrolyte composition typically comprises from about 5 to about 25 weight percent of an inorganic ion salt based on the total weight of the electrolyte, preferably, from about 9 to about 20 weight percent.

The electrolyte composition typically comprises from about 40 to about 80 weight percent of the electrolyte solvent based on the total weight of the electrolyte, preferably from about 60 to about 80 weight percent, and even more preferably about 70 weight percent.

The solid polymeric matrix can contain up to 95 percent, but typically comprises from about 5 to about 30 percent of polysiloxane acrylate. Preferably, the solid polymeric matrix contains from about 15 to about 25 percent of polysiloxane acrylate.

The solid polymeric matrix including the polysiloxane acrylate can be a random or block copolymer. The polysiloxane acrylate preferably is an elastomeric structure containing "comb" structures. Other polysiloxane polymeric structures are also useful in the invention, including linear, cyclic and resinous structures.

In a preferred embodiment, the electrolyte composition further comprises a small amount of a film forming agent. Suitable film forming agents are well known in the art and include, by way of example, polypropylene oxide, polyethylene oxide, copolymers thereof, and the like, having a number average molecular weight of at least about 100,000. Preferably, the film forming agent is employed in an amount of from about 1 to about 10 weight percent and more preferably from about 2 to about 4 weight percent based on the total weight of the electrolyte composition.

The composition may be cured by heating to form a solid film. However, the presence of the polysiloxane acrylate in the composition allows curing by actinic (e.g. UV or EB) radiation. When the composition is cured by heating or UV radiation, the composition preferably contains an initiator. For example, when curing is by heating, the initiator is typically a peroxide such as benzoyl peroxide, methyl ethyl ketone peroxide, t-butyl peroxypyvarate, diisopropyl peroxycarbonate, and the like. When curing is by UV radiation, the initiator is typically benzophenone, Darocur 1173 (Ciby Geigy, Ardsley, N.Y.), and the like. The initiator is generally employed in an amount sufficient to catalyze the polymerization reaction. Preferably, the initiator is employed at up to about 1 weight percent based on the weight of the solid matrix forming monomer. When curing is by EB treatment, an initiator is not required.

The resulting solid electrolyte is a homogeneous, single phase material which is maintained upon curing. See, for example, U.S. Pat. No. 4,925,751 which is incorporated herein by reference in its entirety.

Additionally, it is desirable to avoid the use of any protic materials which will be incorporated into the battery. For example, most of the protic inhibitors for preventing premature monomer polymerization (e.g., protic inhibitors found in di-and triacrylate monomers) employed with the monomers are preferably removed prior to formation of the solid matrix (e.g., the cathode and/or electrolyte) by contact with a inhibitor remover such as Inhibitor Remover available as product number 31,133-2 from Aldrich Chemical, Milwaukee, Wis. Such processes generally will lower the inhibitor concentration to less than about 50 ppm.

In a preferred embodiment, the process of forming an electrolytic cell comprises the steps of coating the surface of a cathode with a composition comprising requisite amounts of a polysiloxane acrylate or a mixture of polysiloxane acrylates, one or more other prepolymers, an inorganic ion salt and the electrolyte solvent. The composition is then cured to provide for a solid electrolyte on the cathodic surface. The anode (e.g., a lithium foil) is then laminated to this composite product in such a way that the solid electrolyte is interposed between the lithium foil and the cathodic material.

This process can be reversed so that the surface of the anode is coated with a composition comprising requisite amounts of a polysiloxane acrylate or a mixture of polysiloxane acrylates, an inorganic ion salt and the electrolyte solvent. The composition is then cured to provide for a solid electrolyte on the anodic surface. The cathode is then laminated to this composite product in such a way that the solid electrolyte is interposed between the lithium foil and the cathodic material.

Methods for preparing solid electrolytes and electrolytic cells are also set forth in U.S. Pat. Nos. 4,830,939 and 4,925,751 which are incorporated herein by reference in their entirety.

The following examples are offered to illustrate the methodology of the invention and should not be construed in any way as limiting its scope.

EXAMPLE 1 A. The Cathode

The cathode may be prepared from a cathodic paste which, in turn, is prepared from a cathode powder as follows:

i. Cathode Powder

The cathode powder is prepared by combining 90.44 weight percent V₆ O₃ [prepared by heating ammonium metavanadate (NH₄ ⁺ VO₃ ⁻) at 450° C. for 16 hours under N₂ flow] and 9.56 weight percent of carbon (from Chevron Chemical Company, San Ramon, Calif. under the trade name of Shawinigan Black®). There is about 100 grams of the resulting mixture placed into a grinding machine (Attritor Model S-1 purchased from Union Process, Akron, Ohio) and ground for 45 minutes. Afterwards, the resulting mixture is dried at about 260° C. for 16 hours under vacuum to provide a cathode powder having about 84.45 weight percent V₆ O₁₃.

The above mixing procedure is repeated until the entire sample is mixed so as to provide for 292 grams of cathode powder.

ii. Cathode Paste

A cathode paste is prepared by combining sufficient cathode powder to provide for a final product having 45 weight percent V₆ O₁₃.

Specifically, there is about 26.2 grams of unground carbon (from Chevron Chemical Company, San Ramon, Calif. under the trade name of Shawinigan Black®) combined in a glove box [under dry (<10 ppm H₂ O) argon at ambient temperature and pressure] with about 169.9 grams of the 4:1 mixture of propylene carbonate/triglyme and the resulting composite is mixed under dry argon and at ambient temperature and pressure on a double planatory mixer (Ross #2 mixer available from Charles Ross & Sons, Company, Hauppag, N.Y.) at about 25 rpms until a paste is formed.

There is about 5 grams of polyethylene oxide (number average molecular weight about 600,000 available as Polyox WSR-205 from Union Carbide Chemicals and Plastics, Danbury, Conn.), about 42.5 grams of polyethylene glycol diacrylate (molecular weight about 400 available as SR-344 from Sartomer Company, Inc., Exton, Pa.) and containing less than about 50 ppm of inhibitor, and about 7.5 grams of ethoxylated trimethylpropane triacrylate (TMPEOTA) (molecular weight about 450, available as SR-454 from Sartomer Company, Inc., Exton, Pa.) and containing less than about 50 ppm of inhibitor, added to about 169.9 grams of a 4: 1 mixture of propylene carbonate/triglyme as described above, and this mixture is then added to the unground carbon and propylene carbonate/triglyme paste in the mixer.

There is about 225.0 grams of a cathode powder prepared in a manner similar to that described above then added to the mixer and the resulting mixture is thoroughly mixed to provide the cathode paste having the following approximate weight percent of components:

    ______________________________________                                         V.sub.6 O.sub.13     45.00 weight percent                                      Carbon               10.00 weight percent                                      Propylene carbonate  27.18 weight percent                                      Triglyme             6.80 weight percent                                       Polyethylene glycol  8.51 weight percent                                       diacrylate                                                                     Ethoxylated trimethylpropane                                                                        1.51 weight percent                                       triacrylate.sup.1                                                              Polyethylene oxide   1.00 weight percent                                       ______________________________________                                          .sup.1 Inhibitor may be removed from both the polyethylene glycol              diacrylate and ethoxylated trimethylpropane triacrylate by contacting eac      of these compounds with an Inhibitor Remover available as Product No.          31,1332 from Aldrich Chemical, Milwaukee, Wisconsin, which results in les      than 50 ppm of inhibitor in the product.                                 

The cathode paste prepared as above is placed onto a sheet [about 1 mil (˜25 μm) thick by 10 cm wide]of a roughened nickel on nickel current collector (available as CF18/NiT from Fukuda Metal Foil & Powder Company, Ltd., Kyoto, Japan). A polyester film cover sheet (for example Mylar®) is then placed over the paste and the paste is spread to a thickness of about 75 μm with a conventional plate and roller system and cured by continuously passing the sheet through an electron beam apparatus (Electrocurtain, Energy Science Inc., Woburn, Mass.) at a voltage of about 175 kV and a current of about 12 mA and at a conveyor belt speed setting of 50 which provides a conveyor speed of about 3 in/sec. After curing, the Mylar® sheet is removed to provide for a solid cathode laminated to a nickel on nickel current collector.

B. Electrolyte

An electrolyte may be prepared by first combining 56.51 grams of propylene carbonate, 14.13 grams triglyme and 17.56 grams of polydimethylsiloxane acrylate having a number average molecular weight of 6,000. The propylene carbonate/triglyme/polydimethyl- siloxane acrylate mixture is dried over molecular sieves (Grade 514, 4Å, 8-12 mesh, available from W.R. Grace, Baltimore, Md.) to remove water.

This solution is then combined with 2.56 grams of poly- ethylene oxide (weight average molecular weight about 600,000 available as Polyox WSR-205 from Union Carbide Chemicals and Plastics, Danbury, Conn.).

The mixture is then thoroughly mixed with the same laboratory mixer at heating until a temperature of about 65 ° C. is reached and then cooled to ambient temperature over at least a 2 hour period while stirring is maintained.

Once the polyethylene oxide is dispersed and dissolved, 9.24 grams of LiPF₆ (available from Hashimoto Chemical Corporation, Osaka, Japan) are added while stirring with a laboratory mixer (Yamato Model LR41B, available from Fisher Scientific, Santa Clara, Calif.).

The resulting mixture would contain the following weight percent of components:

    ______________________________________                                         Propylene carbonate  56.51 weight percent                                      Triglyme             14.13 weight percent                                      Polydimethylsiloxane acrylate                                                                       17.56 weight percent                                      LiPF.sub.6           9.24 weight percent                                       Polyethylene oxide   2.57 weight percent                                       ______________________________________                                    

Afterwards, the electrolyte mixture is then coated by a conventional knife blade to a thickness of about 50 μm onto the surface of the cathode sheet prepared as above (on the side opposite that of the current collector) but without the Mylar® covering. The electrolyte is then cured by continuously passing the sheet through an electron beam apparatus (Electrocurtain, Energy Science Inc., Woburn, Mass.) at a voltage of about 175 kV and a current of about 1.0 mA and at a conveyor speed setting of 50 which provides for a conveyor speed of about 1 cm/sec. After curing, a composite is recovered which contains a solid electrolyte laminated to a solid cathode which, in turn, is laminated to a nickel on nickel current collector. The solid electrolyte had a tendency to separate solvent from the matrix, but otherwise functions satisfactorily.

C. Anode

The anode may comprise a sheet of lithium foil (51 or 76 μm thick) which is commercially available from FMC Corporation Lithium Division, Bessemer City, N.C.

EXAMPLE 2

A solid electrolytic cell is prepared by first preparing a cathode paste which is spread onto a current collector and is then cured to provide for the cathode. An electrolyte solution is then placed onto the cathode surface and is cured to provide for the solid electrolyte composition. Then, the anode is laminated onto the solid electrolyte composition to provide for a solid electrolytic cell. The specifics of this construction are as follows:

A. The Current Collector

The current collector employed is a sheet of aluminum foil having a layer of adhesion promoter attached to the surface of the foil which will contact the cathode so as to form a composite having a sheet of aluminum foil, a cathode and a layer of adhesion promoter interposed therebetween.

Specifically, the adhesion promoter layer is prepared as a dispersed colloidal solution in one of two methods. The first preparation of this colloidal solution for this example is as follows:

    ______________________________________                                         84.4  weight percent of carbon powder (Shawinigan Black ®                        available from Chevron Chemical Company, San Ramon,                            CA)                                                                      337.6 weight percent of a 25 weight percent solution of                              polyacrylic acid (a reported average molecular weight of                       about 90,000, commercially available from Aldrich                              Chemical Company - contains about 84.4 grams                                   polyacrylic acid and 253.2 grams water)                                  578.0 weight percent of isopropanol.                                           ______________________________________                                    

The carbon powder and isopropanol are combined with mixing in a conventional high shear colloid mill mixer (Ebenbach-type colloid mill) until the carbon is uniformly dispersed and the carbon particle size is smaller than 10 microns. At this point, the 25 weight percent solution of polyacrylic acid is added to the solution and mixed for approximately 15 minutes. The resulting mixture is pumped to the coating head and roll coated with a Meyer rod onto a sheet of aluminum foil (about 9 inches wide and about 0.0005 inches thick). After application, the solution/foil are contacted with a Mylar® wipe (about 0.002 inches thick by about 2 inches and by about 9 inches wide--the entire width of aluminum foil). The wipe is flexibly engaged with the foil (i.e., the wipe merely contacted the foil) to redistribute the solution so as to provide for a substantially uniform coating. Evaporation of the solvents (i.e., water and isopropanol) via a conventional gas-fired oven provides for an electrically-conducting adhesion-promoter layer of about 6 microns in thickness of about 3×10⁻⁴ grams per cm². The aluminum foil is then cut to about 8 inches wide by removing approximately 1/2 inch from either side by the use of a conventional slitter so as to remove any uneven edges.

In order to further remove the protic solvent from this layer, the foil is redried. In particular, the foil is wound up and a copper support placed through the roll's cavity. The roll is then hung overnight from the support in a vacuum oven maintained at about 130° C. Afterwards, the roll is removed. In order to avoid absorption of moisture from the atmosphere, the roll is preferably stored into a desiccator or other similar anhydrous environment to minimize atmospheric moisture content until the cathode paste is ready for application onto this roll.

The second preparation of this colloidal solution comprises mixing 25 lbs of carbon powder (Shawinigan Black®--available from Chevron Chemical Company, San Ramon, Calif.) with 100 lbs of a 25 weight percent solution of polyacrylic acid (average molecular weight of about 240,000, commercially available from BF Goodrich, Cleveland, Ohio, as Good-Rite K702--contains about 25 lbs polyacrylic acid and 75 lbs water) and with 18.5 lbs of isopropanol. Stirring is done in a 30 gallon polyethylene drum with a gear-motor mixer (e.g., Lightin Labmaster Mixer, model XJ-43, available from Cole-Parmer Instruments Co., Niles, Ill.) at 720 rpm with two 5 inch diameter A310-type propellers mounted on a single shaft. This wets down the carbon and eliminates any further dust problem. The resulting weight of the mixture is 143.5 lbs and contains some "lumps".

The mixture is then further mixed with an ink mill which consists of three steel rollers almost in contact with each other, turning at 275,300, and 325 rpms respectively. This high shear operation allows particles that are sufficiently small to pass directly through the rollers. Those that do not pass through the rollers continue to mix in the ink mill until they are small enough to pass through these rollers. When the mixing is complete, the carbon powder is completely dispersed. A Hegman fineness of grind gauge (available from Paul N. Gardner Co., Pompano Beach, Fla.) indicates that the particles are 4-6 μm with the occasional 12.5 μm particles. The mixture can be stored for well over 1 month without the carbon settling out or reagglomerating.

When this composition is to be used to coat the current collector, an additional 55.5 lbs of isopropanol is mixed into the composition working with 5 gallon batches in a plastic pail using an air powered shaft mixer (Dayton model 42231 available from Granger Supply Co., San Jose, Calif.) with a 4 inch diameter Jiffy-Mixer brand impeller (such as an impeller available as Catalog No. G-04541-20 from Cole Parmer Instrument Co., Niles, Ill.). Then, it is gear pumped through a 25 μm cloth filter (e.g., So-Clean Filter Systems, American Felt and Filter Company, Newburgh, N.Y.) and Meyer-rod coated as described above.

B. The Cathode

The cathode is prepared from a cathodic paste which, in turn, is prepared from a cathode powder as follows:

i. Cathode Powder

The cathode powder is prepared by combining 90.44 weight percent V₆ O₁₃ [prepared by heating ammonium metavanadate (NH₄ ⁺ VO₃ ⁻) at 450° C. for 16 hours under N₂ flow] and 9.56 weight percent of carbon (from Chevron Chemical Company, San Ramon, Calif. under the tradename of Shawinigan Black®). About 100 grams of the resulting mixture is placed into a grinding machine (Attritor Model S-1 purchased from Union Process, Akron, Ohio) and ground for 30 minutes. Afterwards, the resulting mixture is dried at about 260° C. for 21 hours.

ii. Cathode Paste

A cathode paste is prepared by combining sufficient cathode powder to provide for a final product having 45 weight percent V₆ O₁₃.

Specifically, 171.6 grams of a 4:1 weight ratio of propylene carbonate:triglyme is combined with 42.9 grams of polyethylene glycol diacrylate (molecular weight about 400 available as SR-344 from Sartomer Company, Inc., Exton, Pa.), and about 7.6 grams of ethoxylated trimethylolpropane triacylate (TMPEOTA) (molecular weight about 450 available as SR-454 from Sartomer Company, Inc., Exton, Pa.) in a double planetary mixer (Ross #2 mixer available from Charles Ross & Sons, Company, Hauppag, N.Y.).

A propeller mixture is inserted into the double planetary mixer and the resulting mixture is stirred at a 150 rpms until homogeneous. The resulting solution is then passed through sodiated 4Å molecular sieves. The solution is then returned to double planetary mixer equipped with the propeller mixer and about 5 grams of polyethylene oxide (number average molecular weight about 600,000 available as Polyox WSR-205 from Union Carbide Chemicals and Plastics, Danbury, Conn.) is added to the solution vortex from by the propeller by a mini-sieve such as a 25 mesh mini-sieve commercially available as Order No. 57333-965 from VWR Scientific, San Francisco, Calif.

The solution is then heated while stirring until the temperature of the solution reaches 65° C. At this point, stirring is continued until the solution is completely clear. The propeller blade is removed and the carbon powder prepared as above is then is added as well as an additional 28.71 grams of unground carbon (from Chevron Chemical Company, San Ramon, Calif. under the tradename of Shawinigan Black®). The resulting mixture is mixed at a rate of 7.5 cycles per second for 30 minutes in the double planetary mixer. During this mixing the temperature is slowly increased to a maximum of 73° C. At this point, the mixing is reduced to 1 cycle per second the mixture slowly cooled to 40° C. to 48° C. (e.g. about 45° C.). The resulting cathode paste is maintained at this temperature until just prior to application onto the current collector.

The resulting cathode paste has the following approximate weight percent of components:

    ______________________________________                                         V.sub.6 O.sub.13      45 weight percent                                        Carbon                10 weight percent                                        4:1 propylene carbonate/triglyme                                                                     34 weight percent                                        Polyethylene oxide    1 weight percent                                         Polyethylene glycol diacrylate                                                                       8.5 weight percent                                       ethoxylated trimethylol-                                                                             1.5 weight percent                                       propane triacrylate                                                            ______________________________________                                    

In an alternative embodiment, the requisite amounts of all of the solid components may be added directly to combined liquid components. In this regard, mixing speeds can be adjusted to account for the amount of the material mixed and size of vessel used to prepare the cathode paste. Such adjustments are well known to the skilled artisan.

In order to enhance the coatability of the carbon paste onto the current collector, it may be desirable to heat the paste to a temperature of from about 60° C. to about 130° C. and more preferably, from about 80° C. to about 90° C. and for a period of time of from about 0.1 to about 2 hours, more preferably, from about 0.1 to 1 hour and even more preferably from about 0.2 to 1 hour. A particularly preferred combination is to heat the paste at from about 80° C. to about 90° C. for about 0.33 to about 0.5 hours.

During this heating step, there is no need to stir or mix the paste although such stirring or mixing may be conducted during this step. However, the only requirement is that the composition be heated during this period. In this regard, the composition to be heated has a volume to surface area ratio such that the entire mass is heated during the heating step.

A further description of this heating step is set forth in U.S. patent application Ser. No. 07/968,203, filed Oct. 29, 1992, and entitled "METHODS FOR ENHANCING THE COATABILITY OF CARBON PASTES TO SUBSTRATES", which application is incorporated herein by reference in its entirety.

The so-prepared cathode paste is then placed onto the adhesion layer of the current collector described above by extrusion at a temperature of from about 45° to about 48° C. A Mylar® cover sheet is then placed over the paste and the paste is spread to thickness of about 90 microns (μm) with a conventional plate and roller system and is cured by continuously passing the sheet through an electron beam apparatus (Electrocurtain, Energy Science Inc., Woburn, Mass.) at a voltage of about 175 kV and a current of about 1.0 mA and at a rate of about 1 cm/sec. After curing, the Mylar® sheet is removed to provide for a solid cathode laminated to the aluminum current collector described above.

C. Electrolyte

An amount of 56.51 grams of propylene carbonate, 14.13 grams of triglyme and 17.56 grams of polydimethylsiloxane acrylate having a number average molecular weight of about 6,000 are combined at room temperature until homogeneous. The resulting solution is passed through a column of 4Å to remove water and then mixed at room temperature until homogeneous.

At this point, 2.57 grams of polyethylene oxide (PEO) film forming agent having a number average molecular weight of about 600,000 (available as Polyox WSR-205 from Union Carbide Chemicals and Plastics, Danbury, Conn.) is added to the solution and then dispersed while stirring with a magnetic stirrer over a period of about 30 minutes. After dispersion, the solution is heated to between 60° C. and 65° C. with stirring until the film forming agent dissolves. The solution is cooled to a temperature of between 45° and 48° C., a thermocouple is placed at the edge of the vortex created by the magnetic stirrer to monitor solution temperature, and then 9.24 grams of LiPF₆ are added to the solution over a 30 minute period while thoroughly mixing to ensure a substantially uniform temperature profile throughout the solution. Cooling is applied as necessary to maintain the temperature of the solution no greater than 50°.

In one embodiment, the polyethylene oxide film forming agent is added to the solution via a mini-sieve such as a 25 mesh mini-sieve commercially available as Order No. 57333-965 from VWR Scientific, San Francisco, Calif.

The resulting solution contains the following:

    ______________________________________                                         Component        Amount   Weight Percent.sup.2                                 ______________________________________                                         Propylene carbonate                                                                             56.51 g  56.51                                                Triglyme         14.13 g  14.13                                                Polydimethylsiloxane                                                                            17.56 g  17.56                                                Acrylate                                                                       LiPF.sub.6       9.24 g   9.24                                                 PEO film forming agent                                                                          2.56 g   2.56                                                 Total            100 g    100                                                  ______________________________________                                          .sup.2 = weight percent based on the total weight of the electrolyte           solution (100 g).                                                        

This solution is then degassed to provide for an electrolyte solution wherein little, if any, of the LiPF₆ salt decomposes.

Optionally, solutions produced as above and which contain the polydimethylsiloxane acrylate, the polyalkylene oxide film forming agent, the electrolyte solvent and the LiPF₆ salt are filtered to remove any solid particles or gels remaining in the solution. One suitable filter device is a sintered stainless steel screen having a pore size between 1 and 50 μm at 100% efficiency.

Alternatively, the electrolyte solution can be prepared in the following manner. Specifically, in this example, the mixing procedure is conducted using the following weight percent of components:

    ______________________________________                                         Propylene carbonate 52.472 weight percent                                      Triglyme            13.099 weight percent                                      Polydimethylsiloxane Acrylate                                                                      20.379 weight percent                                      LiPF.sub.6          10.720 weight percent                                      PEO film forming agent.sup.3                                                                       3.340 weight percent                                       ______________________________________                                          .sup.3 Polyethylene oxide film forming agent having a number average           molecular weight of about 600,000 (available as Polyox WSR205 from Union       Carbide Chemicals and Plastics, Danbury, CT)                             

The mixing procedure employs the following steps:

1. Check the moisture level of the polydimethylsiloxane acrylate. If the moisture level is less than 100 ppm water, proceed to step 2. If not, then first dissolve the polysiloxane acrylate at room temperature, <30° C., in the propylene carbonate and triglyme and dry the solution over sodiated 4Å molecular sieves (Grade 514, 8-12 Mesh from Schoofs Inc., Moraga, Calif.). Proceed to step 4.

2. Dry the propylene carbonate and triglyme over sodiated 4Å molecular sieves (Grade 514, 8-12 Mesh from Schoofs Inc., Moraga, Calif.).

3. At room temperature, <30° C., add the polydimethylsiloxane monomer to the solvent prepared in step 2. Stir at 300 rpm until the resin is completely dissolved. The solution should be clear.

4. Dry and then sift the polyethylene oxide film forming agent through a 25 mesh mini-sieve commercially available as Order No. 57333-965 from VWR Scientific, San Francisco, Calif. While stirring at 300 rpm, add the dried and presifted polyethylene oxide film forming agent slowing to the solution. The polyethylene oxide film forming agent is sifted into the center of the vortex formed by the stirring means over a 30 minute period. Addition of the polyethylene oxide film forming agent is dispersive and, during addition, the temperature is maintained at room temperature (<30° C.).

5. After final addition of the polyethylene oxide film forming agent, stir an additional 30 minutes to ensure that the film forming agent is substantially dispersed.

6. Heat the mixture to 68° C. to 75° C. and stir until the film forming agent has melted and the solution has become transparent to light yellow in color. Optionally, in this step, the mixture is heated to 65° C. to 68° C.

7. Cool the solution produced in step 6 and when the temperature of the solution reaches 40° C., add the LiPF₆ salt very slowly making sure that the maximum temperature does not exceed 55° C.

8. After the final addition of the LiPF₆ salt, stir for an additional 30 minutes, degas, and let sit overnight and cool.

9. Filter the solution through a sintered stainless steel screen having a pore size between 1 and 50 μm at 100% efficiency.

At all times, the temperature of the solution should be monitored with a thermocouple which should be placed in the vortex formed by the mixer.

Afterwards, the electrolyte mixture is then coated by a conventional knife blade to a thickness of about 50 μm onto the surface of the cathode sheet prepared as above (on the side opposite that of the current collector) but without the Mylar® covering. The electrolyte is then cured by continuously passing the sheet through an electron beam apparatus (Electrocurtain, Energy Science Inc., Woburn, Mass.) at a voltage of about 175 kV and a current of about 1.0 mA and at a conveyor speed setting of 50 which provides for a conveyor speed of about 1 cm/sec. After curing, a composite is recovered which contains a solid electrolyte laminated to a solid cathode. The matrix showed a tendency to separate from the electrolyte solvent, but this would not prevent the solid electrolytic from functioning.

D. Anode

The anode comprises a sheet of lithium foil (51 or 76 μm thick) which is commercially available from FMC Corporation Lithium Division, Bessemer City, N.C.

While the invention has been described in terms of various preferred embodiments, the skilled artisan will appreciate that various modifications, substitutions, omissions, and changes may be made without departing from the spirit thereof. The descriptions of subject matter in this disclosure are illustrative of the invention and are not intended to be construed as limitations upon the scope of the invention. 

What is claimed is:
 1. A solid electrolyte comprising:a solid polymeric matrix; an electrolyte solvent; and an inorganic ion salt; wherein said solid polymeric matrix comprises a polymerized polysiloxane acrylate.
 2. A solid electrolyte according to claim 1 wherein said polysiloxane acrylate is polymerized by exposure to actinic radiation.
 3. A solid electrolyte according to claim 1 wherein said polysiloxane acrylate is the reaction product of the acrylic acid represented by Formula I:

    CH.sub.2 =CR.sup.1 C(O)OH

wherein R¹ is H or an alkyl group of from 1 to 4 carbon atoms, and polysiloxane.
 4. A solid electrolyte according to claim 1 wherein said polysiloxane acrylate is of molecular average molecular weight of from about 150 to about 5,000.
 5. A solid electrolyte according to claim 1 wherein said polysiloxane acrylate is the reaction product of an acrylic acid and a polysiloxane consisting essentially of from about 3 to about 50 repeating units selected from the group consisting of: ##STR3## and mixtures thereof, wherein R¹ and R² are independently alkyl groups of from 1 to 4 carbon atoms, R³ is an alkylene group of from 1 to 4 carbon atoms, R⁴ is an alkylene group of from 1 to 6 carbon atoms, and n is 0 or an integer from 1 to
 50. 6. A solid electrolyte according to claim 1 wherein said polysiloxane acrylate is co-polymerized with at least one other polymer precursor selected from the group consisting of: polyethylene oxide, polypropylene oxide, polyethyleneimine, polyepichlorohydrin, and an acryloyl-derivitized poly(oxyalkylene) oxide.
 7. An electrochemical cell comprises:an anode compound composed of a compatible anodic material; a cathode composed of compatible cathodic material; and interposed therebetween, a solid electrolyte comprising, a solid polymeric matrix; an electrolyte solvent; and an inorganic ion salt; wherein said polymeric matrix comprises a polymerized polysiloxane acrylate.
 8. A battery comprising a plurality of the electrochemical cell of claim
 7. 9. A method of making a solid electrolyte comprising the steps of forming a mixture comprising a compatible electrolyte solvent, an inorganic ion salt, and a polysiloxane acrylate, and exposing said mixture actinic-radiation. 